Effect of Cr and Zr Dopes on Hydrogen Behaviour in Rapidly Solidified Aluminium Foils

Hydrogen (H) behaviour in materials was investigated in rapidly solidified (RS) foils of pure aluminium (Al), Al-0.4 Cr and Al-0.25 Zr alloys (at %) by means of thermal desorption spectroscopy (TDS). In addition, Al-0.25; 0.3 Zr alloys were examined with respect to microstructure and its instability during the thermal process using SEM and microhardness measurements. The effect of dopes and heating rate on H desorption was summarized. The lowest energy desorption is attributed with significant thermal desorption peak which temperature was found is correlated with sample composition.