Raman spectroscopic studies of the polymorphism in ZrO2 at high pressures

The Raman spectra of Zro2 at high pressures are measured at room temperature using a diamondanvil pressure-cell. Two kinds of pressure transmitting medium, methanol and Nacl, are used to see the effect of stress components on the phase transformation. The pressure of phase transformation shows a considerable difference between the two media. In the case of methanol, a phase transformation is observed at 3.5 Gpa, while in the case of Nacl, at 5.4 GPa. In the high-pressure phase, 19 Raman bands are observed. This number of bands far exceeds that which is expected for the tetragonal phase, D in space group. From the relation between the number of Raman bands and the crystal structure, it is more reasonable to consider that the high-pressure phase belongs to a orthorhombic system. The space group of the high-pressure phase is discussed on the basis of the observed number of Raman bands. Les spectres de Raman de Zro2 à haute pression ont été mesurés æ la température ordinaire en utilisant la cellule d'enclume diamant. Deux sortes de pression transmettrant matiére, méthanol et NaCl ont été utilisé pour estimer l'effet du stress sur la transformation de phase. En cas du méthanol, la transformation de phase a été observé æ 3,5 GPa. Mais, en cas du Nacl, cette transformation a été observé æ 5,4 GPa. A haute pression, 19 bandes de Raman ont été observes. Ce nombre de band de Raman excéde celui de phase tetragonal dont le groupe d'espace est D. En considerent le nombre de band de Raman, il est raisonable que la phase a haute pression appartienne au systéme orthorhombique.