Corroded Nitinol Wires in Explanted Aortic Endografts: An Important Mechanism of Failure?

Corrosion of the nitinol wire in endovascular grafts is confirmed. Presumably, the observed pitting and irregularly shaped corrosion defects are the precursors of material failure. They weaken the thin wire, which leads to stress cracks and eventually fracture of the stent wire under circulatory pulsation. Cell-induced electrochemical corrosion and active cellular destruction of surfaces are well-known mechanisms that must be investigated for their possible roles in the corrosion of stent metals.