Oxygen-Dependent Instability and Annealing/Passivation Effects in Amorphous In–Ga–Zn–O Thin-Film Transistors

This letter discusses the reason for the instability of amorphous indium-gallium-zinc-oxide (a-IGZO) thin-film transistors (TFTs) under both positive and negative bias stresses. This instability is significantly influenced by the oxygen content in the bulk IGZO and the surrounding environment. The as-fabricated low-temperature devices can only endure a single polarized bias stress. An a-IGZO TFT that is stable toward both positive and negative bias stresses with large relaxation times of 95 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sup> and 371 × 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sup> s, respectively, is achieved by annealing and passivation.