Low‐Temperature Fabrication of Transparent Yttrium Aluminum Garnet (YAG) Ceramics without Additives

A carbonate precursor of yttrium aluminum garnet (YAG) with an approximate composition of NH 4 AlY 0.6 (CO 3 ) 1.9 (OH) 2 ·0.9H 2 O was synthesized via a coprecipitation method from a mixed solution of ammonium aluminum sulfate and yttrium nitrate, using ammonium hydrogen carbonate as the precipitant. The precursor precipitate was characterized using chemical analysis, differential thermal analysis/thermogravimetry, X‐ray diffractometry, and scanning electron microscopy. The sinterability of the YAG powders was evaluated by sintering at a constant rate of heating in air and vacuum sintering. The results showed that the precursor completely transforms to YAG at ∼1000°C via the formation of a yttrium aluminate perovskite (YAP) phase. YAG powders obtained by calcining the precursor at temperatures of ≤1200°C were highly sinterable and could be densified to transparency under vacuum at 1700°C in 1 h without additives.