Physical-Mechanical Properties of Glued Laminated Timber Made from Tropical Small-Diameter Logs Grown in Indonesia

The aim of this study was to determine the physical and mechanical properties of glued laminated timber (glulam) manufactured from small-diameter logs of three wood species, Acacia mangium (mangium), Maesopsis eminii (manii), and Falcataria moluccana (sengon), with densities of 533, 392, and <TEX>$271kg/m^3$</TEX>, respectively. Glulam measuring 5 cm by 7 cm by 160 cm in thickness, width, and length, respectively, was made with three to five lamina, or layers, and isocyanate adhesive. The glulams contained either the same wood species for all layers or a combination of mangium face and back layers with a core layer of manii or sengon. Solid wood samples of the same size for all three species were included as a basis for comparison. Physical-mechanical properties and delamination tests of glulam referred to JAS 234:2003. The results showed that the properties of same species glulam did not differ from those of solid wood, with the exception of the shear strength of glulam being lower than that of solid wood. Wood species affected glulam properties, but three- and five-layer glulams were not different except for the modulus of elasticity. All glulams were resistant to delamination by immersion in both cold and boiling water. The glulams that successfully met the JAS standard were three- and five-layer mangium, five-layer manii, and five-layer mangium-manii glulams.