Evolution of Lattice Spacing of Gamma Double Prime Precipitates During Aging of Polycrystalline Ni-Base Superalloys: An In Situ Investigation

Abstract Polycrystalline Ni-base superalloy Inconel 718 derives the strengthening mainly from Ni 3 Nb γ ″ phase. To investigate the evolution of lattice spacing of γ ″ precipitates, in situ neutron diffraction experiments were performed during aging heat treatment of two Inconel 718 bar samples at 780 °C for 8 hours. One sample was aged with a negligible applied stress (5 MPa) and the other with an applied tensile stress of 300 MPa. The diffraction data demonstrate three stages of lattice spacing evolution due to compositional and morphological changes during aging. (1) Stage I, the γ lattice spacing decreases isotropically in the first hour of aging as the composition changes. (2) Stage II, the γ lattice spacing decreases and the γ ″ lattice spacing increases between 1 and 5 hours of aging, at this stage compositional change on the lattice evolution weakens with aging time and the morphological change becomes comparable. (3) Stage III, as aging proceeds, compositional change is negligible, while morphological change is dominant; the γ lattice spacing decreases in the longitudinal direction but increases in the transverse direction; in contrast, the converse occurs in γ ″ lattice spacing evolution.