Development of Wood Polymer Composites from Recycled Wood and Plastic Waste: Thermal and Mechanical Properties

The depletion of natural resources due to the aggressive industrialization in the last decades has brought considerable attention to research aimed at developing green and sustainable products using eco-friendly materials. The purpose of the current study was to develop wood polymer composites (WPCs) using recycled plastic waste (RPW) generated from university laboratories and recycled wood waste (RWW) from construction and demolition (C&D) activities by melt-blending technique. The WPCs were characterised for their mechanical and thermal properties, as well as water uptake and morphology. The SEM micrograph indicated good interaction between RWW and RPW matrix. The mechanical strength of the WPCs was found to increase from 26.59 to 34.30 MPa, with an increase of the RWW content in the matrix. The thermal stability was higher in the composite with a higher percentage of RWW in the matrix. The wettability results indicated that the composite with a higher RWW (20%) had a higher water uptake. These results suggest that the produced WPCs can be a promising environmental-friendly material, while maintaining good mechanical, thermal, and wettability properties.