Ion-Induced Polysaccharide Gelation: Peculiarities of Alginate Egg-Box Association with Different Divalent Cations

Structural aspects of polysaccharide hydrogels based on sodium alginate and divalent cations Ba²⁺, Ca²⁺, Sr²⁺, Cu²⁺, Zn²⁺, Ni²⁺ and Mn²⁺ was studied using data on hydrogel elemental composition and combinatorial analysis of the primary structure of alginate chains. It was shown that the elemental composition of hydrogels in the form of freezing dried microspheres gives information on the structure of junction zones in the polysaccharide hydrogel network, the degree of filling of egg-box cells by cations, the type and magnitude of the interaction of cations with alginate chains, the most preferred types of alginate egg-box cells for cation binding and the nature of alginate dimers binding in junction zones. It was ascertained that metal-alginate complexes have more complicated organization than was previously desired. It was revealed that in metal-alginate hydrogels, the number of cations of various metals per C12 block may be less than the limiting theoretical value equal to 1 for completely filled cells. In the case of alkaline earth metals and zinc, this number is equal to 0.3 for calcium, 0.6 for barium and zinc and 0.65-0.7 for strontium. We have determined that in the presence of transition metals copper, nickel and manganese, a structure similar to an egg-box is formed with completely filled cells. It was determined that in nickel-alginate and copper-alginate microspheres, the cross-linking of alginate chains and formation of ordered egg-box structures with completely filled cells are carried out by hydrated metal complexes with complicated composition. It was found that an additional characteristic of complex formation with manganese cations is the partial destruction of alginate chains. It has been established that the existence of unequal binding sites of metal ions with alginate chains can lead to the appearance of ordered secondary structures due to the physical sorption of metal ions and their compounds from the environment. It was shown that hydrogels based on calcium alginate are most promising for absorbent engineering in environmental and other modern technologies.