Comparison of Nb ₃ Sn Insulation Systems With as Received and De-Sized Glass

Epoxy cracking has been the main suspected contributor to training in Nb3Sn magnets for some time, as it leads to energy release and magnet quenching. Cracking in a superconducting composite can occur from several modes, and the likelihood of these modes is not well understood. Failure has been observed between insulation systems and the superconducting cable itself rather than within the cable or insulation. To target the behavior at the interface, samples have been fabricated and tested for Mode I fracture toughness in an adapted version of ASTM D5528. This work seeks to better characterize the fracture toughness of this interface to better understand how to model and design insulation systems.