Mitigation of Cu-Induced Grain Boundary Sensitization in Steel Wire Rods Through a Desensitization Heat Treatment

Steel wire rods are essential for manufacturing high-strength steel tire cords. Yet, the presence of residual copper (Cu) in recycled steel can cause grain-boundary sensitization, embrittlement, and deterioration of the mechanical performance of the final product. This study introduces a desensitization heat treatment step designed to redistribute Cu away from austenite grain boundaries after sensitization occurs. The treatment consists of a 10 min dwell at 1000 °C in a 5%H2-Ar reducing atmosphere followed by quench. The temperature and hold time were selected based on diffusion calculations to promote solid-state back diffusion of Cu without altering grain morphology. Experimental validation showed that the dwell step reduced the length of Cu-rich sensitized zones of steel wire rod samples containing 0.21 wt.% Cu by approximately 89% and restored the mechanical properties to nearly 95–98% relative to low-Cu baseline steel (0.01 wt.% Cu). Compared with sensitized and as-obtained samples, these results highlight the effectiveness of the proposed method in improving both the microstructure and tensile performance of recycled steel wire rods, enabling their potential application in tire manufacturing.