Phase-field predictions of the influence of cooling rates during AM on the Evolution of Microstructures in Nickel-Based Single Crystal Superalloys

Additive manufacturing of single crystals made of Ni-based superalloys offers major cost savings for gas turbine engines with the inclusion of internal cooling channels. However, the lack of understanding of the effect of transient thermal conditions on solidification grain structure during additive manufacturing hinders the potential for process control to maintain the single crystal quality. The use of high-fidelity simulations through high performance computing to predict the evolution of the solidification microstructure will enhance the abilities to tailor the microstructures through process optimization. Phase field simulations are used to determine the effect local thermal conditions and defects on the stability of the solidification morphology, specifically with respect to the onset of columnar-to-equiaxed transition that results in the loss of the single crystal. The results are expected to be instrumental for developing future surrogate models to speed up the integration of design and manufacturing of turbine blades under the harsh in-service conditions.