Microstructure and Mechanical Properties of PM Ti-4Al-2Fe-3Cu Alloy Modified by Vanadium Addition

This study examines the effect of vanadium addition on the microstructure and mechanical properties of low-cost powder metallurgy Ti-4Al-2Fe-3Cu alloys. Alloys with and without 6 wt.% V were fabricated by hot extrusion of blended elemental powders followed by vacuum heat treatment. Microstructural analysis revealed that the base alloy exhibits a coarse lamellar α/β structure, while vanadium addition promotes a refined basketweave morphology with a significantly higher β-phase fraction, increasing from 28.1% to 46.2%. Energy-dispersive spectroscopy confirmed preferential partitioning of Fe, Cu, and V into the β phase. Mechanical testing showed that the addition of 6 wt.% V markedly enhances strength, increasing yield strength and ultimate tensile strength from 1122 MPa and 1214 MPa to 1291 MPa and 1349 MPa, respectively, while maintaining comparable tensile ductility (~3.5%). The strength improvement is attributed to α-plate refinement, increased β-phase fraction, and solid-solution strengthening of the β phase. These results demonstrate that vanadium addition is an effective approach for improving the strength of low-cost PM titanium alloys without compromising ductility.