Gaseous Hydrogen Embrittlement of L-PBF Ni-Based Superalloys for Service in Natural Gas Turbines

Efforts to improve efficiency of industrial gas turbine engines have focused on increasing operating temperatures by use of fuel-flexible gas blends. Ni-based superalloys are susceptible to hydrogen embrittlement (HE), leading to potential risk of premature component failure. Certain turbine components exposed to hydrogen-rich environments are manufactured from additive processes like laser powder bed fusion (L-PBF). The HE susceptibility was evaluated for three Ni-based superalloys: solid solution strengthened Alloy 625, γ’/γ’’-precipitation strengthened Alloy 718, and γ’-precipitation strengthened Haynes® 282®. L-PBF samples were pre-charged under medium and high pressure gaseous hydrogen before tensile testing at temperatures up to 260 °C using a fast strain rate. Selected samples were subjected to a service conditioning heat treatment prior to hydrogen charging to evaluate the change in susceptibility after prolonged service. The susceptibility to HE and HE mechanisms of these three alloys is compared.